Binding Wire

We can supply super quality hot dipped galvanized wire made of low carbon steel and high carbon steel.

Processing of Hot-dip Galvanized Wire:

Hot-dip galvanized wire is made of high-quality low-carbon steel wire rod, which is made of high-quality low-carbon steel, processed by drawing forming, pickling and rust removal, high-temperature annealing, hot-dip galvanizing and cooling.Hot-dip galvanizing is dip-coating in a heated and melted zinc solution. The production speed is fast and the coating is thick.

Detail

Tags

product description

The minimum thickness allowed by the market is 45 microns, and the maximum thickness can reach more than 300 microns.The color is darker, consumes more zinc metal, forms an infiltration layer with the base metal, and has good corrosion resistance. Hot-dip galvanizing can last for decades in outdoor environments.

Binding Wire

We produces hot-dip galvanized wire from choiced low/high carbon steel wire, through the strict process of wire drawing-annealing-acid washing-water clearing-drying-galvanizing-coiling, in this way, excellent flexibility and tensile strength could be guaranteed.

Technical/Mechanical Characters

Material: SAE1006/1008,Q195/235 SAE1050/1065
Zinc coating: 0.10Oz-1.60Oz/Sq.feet;
Commercial grade:>60grams/sq.m
Heavy coating: >200grams/sq.m >250grams/sq.m

Diameter range: 0.50-4,90mm
T.S.: 300/550Mpa, 350/450Mpa, 450-550Mpa, 600-800Mpa, 700-900Mpa 1100-1300Mpa, 1300-1700Mpa etc.
Packing: 1kg-800kgs/orbit coil

Application

This kind of wire is extensively used in construction, woven mesh, express way fencing, bailing and many other usage.

low carbon steel wire

Diameter ranges

0.50mm to 4.90mm

Zinc Coating

Tensile Strength

Material

Commercial Grade:
> 60g/sq. meter

Heavy zinc coating:
> 200g/sq. meter
> 250g/sq. meter

300-500Mpa
350-450Mpa
450-550Mpa
600-800Mpa
700-900Mpa
1100-1300Mpa
1300-1700Mpa

Q195
Q235
SAE 1006
SAE 1008
SAE 1045
SAE 1060
SAE 1065